The ordering kinetics of standing cylinder-forming polystyrene-block-poly (methyl methacrylate) block copolymers (molecular weight: 39 kg/mol) close to the order-disorder transition is experimentally investigated following the temporal evolution of the correlation length at different annealing temperatures. The grow exponent of the grain coarsening process is determined to be 1/2, signature of a curvature driven ordering mechanism. The measured activation enthalpy and the resulting Meyer-Neldel temperature for this specific copolymer along with the data already known for PS-b-PMMA block copolymers in strong segregation limit, allows investigating the interplay between the ordering kinetics and the thermodynamic driving force during the grain coarsening. These findings unveil various phenomena concomitantly occurring during the thermally activated ordering kinetics at segmental, single chain, and collective level.
Publication date: 
17 Dec 2019

Gabriele Seguini, Fabio Zanenga, Gianluca Cannetti, Michele Perego

Biblio References: 
arXiv preprint arXiv:1912.08120